A high temperature embrittlement occures in Fe-15Cr-4AI and Fe-20Cr-4Al alloys treated over 1000 C.It is caused mainly by 475℃ brittleness during cooling.When a secondary treatment at 500℃ was conducted,the 475℃ brittleness developed very rapidly.After only 15 rain of the treating,little plasticity was remained for all samples pretreuted at the temper- atures over 1000℃ and cooled in water.However,no 475℃ brittleness was generated when pretreating temperature was below 1000℃,Addition of Yttrium can inhibit not only grain growth,but also 475℃ brittleness.For the alloys with 0.2—0.4 wt-%Y,after treating at 800—1300℃,the plasticity did not decrease and the properties of furnace cooled samples were not lower than those of water cooled samples.
关键词:
Fe-Cr-Al alloy
,
null
,
null